Fortron 1140L6 PPS Ticona
Fortron 1140L6 PPS Ticona
Fortron 1140L7 PPS Ticona
Fortron 1140LC6 PPS Ticona
Fortron 1141L4 PPS Ticona
Fortron 1140L6 PPS Ticona 材料物性表如下:
| Physical | Nominal Value | Unit | Test Method |
| Specific Gravity | |||
| -- | 1.60 | g/cm3 | ASTM D792 |
| -- | 1.65 | g/cm3 | ISO 1183 |
| Specific Volume | 0.625 | cm3/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 19 | g/10 min | ASTM D1238 |
| Molding Shrinkage | |||
| Flow | 0.20 to 0.30 | % | ASTM D955 |
| Across Flow | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow | 0.40 to 0.60 | % | ISO 294-4 |
| Flow | 0.20 to 0.60 | % | ISO 294-4 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | ISO 62 |
| Spiral Flow | 21.5 | Internal Method | |
| Hardness | Nominal Value | Unit | Test Method |
| Rockwell Hardness (M-Scale) | 100 | ASTM D785, ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
| Tensile Modulus | 14700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Break, 23°C | 200 | MPa | ASTM D638 |
| Break | 195 | MPa | ISO 527-2/1A/5 |
| Tensile Elongation | |||
| Break, 23°C | 2.0 | % | ASTM D638 |
| Break | 1.9 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 14500 | MPa | ISO 178 |
| Flexural Strength 3 | 285 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 10 | kJ/m2 | |
| 23°C | 10 | kJ/m2 | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C | 53 | kJ/m2 | |
| 23°C | 53 | kJ/m2 | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 10 | kJ/m2 | |
| 23°C | 10 | kJ/m2 | |
| Unnotched Izod Impact Strength (23°C) | 34 | kJ/m2 | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
| Deflection Temperature Under Load | |||
| 0.45 MPa, Annealed | 280 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 265 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 270 | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 215 | °C | ISO 75-2/C |
| Glass Transition Temperature 4 | 90.0 | °C | ISO 11357-2 |
| Melting Temperature 4 | 280 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 0.000026 | cm/cm/°C | |
| Transverse | 0.000042 | cm/cm/°C |
Fortron 1130A1 PPS Polyplastics
Fortron 1130T6 PPS Polyplastics
Fortron 2130A1 PPS Polyplastics
Fortron 3130A1 PPS Polyplastics
:鄧
:86-
傳真號(hào)碼:86-
地址:中國(guó) 廣東 東莞 東莞市 樟木頭鎮(zhèn) 塑膠原料市場(chǎng)
Fortron 1140L6 PPS Ticona玻纖40%其它產(chǎn)品
Fortron 1140L6 PPS Ticona玻纖40%
Fortron 1130L4 PPS Ticona玻纖30%
Fortron 1130L0 PPS Ticona玻纖30%
Fortron 1120L4 PPS Ticona玻纖20%
Fortron 0205 PPS Ticona熱穩(wěn)定
Fortron 0203HS PPS Ticona熱穩(wěn)定
Fortron 7340A4 PPS Polyplastics導(dǎo)電性
Fortron 7300A1 PPS Polyplastics耐磨性
Fortron 6935A4 PPS Polyplastics耐磨性
Fortron 6660A42 PPS Polyplastics原廠原包

















班戈县|
西乌珠穆沁旗|
延寿县|
沙河市|
射洪县|
宁海县|
淮阳县|
偃师市|
东海县|
武义县|
微山县|
同江市|
镇宁|
夏河县|
定兴县|
九龙城区|
鹿泉市|
马龙县|
上高县|
成安县|
黔江区|
莱阳市|
渭南市|
邵阳市|
乌苏市|
确山县|
淳安县|
红安县|
连南|
阿瓦提县|
郓城县|
永靖县|
哈巴河县|
专栏|
滁州市|
宁波市|
葵青区|
兴山县|
中方县|
额济纳旗|
新蔡县|